S5 PTFE Heat Shrink Tube | ||||
Features | ||||
Semi-rigid, cross-linked PTFE | Operating temperature: -80~260 ℃ | |||
Exceptional electrical properties | Shrink temperature: 350 ℃ | |||
High flame retardant | Shrink Ratio:1.7:1 | |||
High temperature protection | ||||
Dimensions | ||||
Reference |
As supplied(mm) |
After recovered(mm) |
Standard length |
|
UPM S5 PTFE |
ID min. |
ID max. |
WT nom. |
m |
0.5 |
0.7±0.2 |
0.4 |
0.20 |
200 |
1.0 |
1.0±0.2 |
0.5 |
0.20 |
200 |
1.5 |
1.5±0.2 |
0.9 |
0.20 |
200 |
2.0 |
2.0±0.2 |
1.3 |
0.20 |
200 |
2.5 |
2.5±0.2 |
1.5 |
0.20 |
200 |
3.0 |
3.0±0.2 |
1.8 |
0.20 |
200 |
3.5 |
3.5±0.2 |
2.0 |
0.20 |
100 |
3.8 |
3.8±0.2 |
2.0 |
0.20 |
100 |
4.0 |
4.0±0.3 |
2.5 |
0.25 |
100 |
4.5 |
4.5±0.3 |
2.8 |
0.25 |
100 |
5.0 |
5.0±0.3 |
3.0 |
0.25 |
100 |
6.0 |
6.0±0.3 |
3.8 |
0.25 |
100 |
7.0 |
7.0±0.3 |
4.0 |
0.25 |
100 |
8.0 |
8.0±0.3 |
4.8 |
0.25 |
1 |
9.0 |
9.0±0.3 |
5.0 |
0.30 |
1 |
ID=Internal Diameter | WT=wall thickness |
Technical Data | ||||
Property | Test method | Values | ||
Physical | Density | ASTM D792 | 2.10~2.29 | |
Water absorption | ASTM D570 | ≤0.1% | ||
Tensile strength | ASTM D2671 | ≥17MPa | ||
Breakdown elongation | ASTM D2671 | ≥200% | ||
Hardness Shore D | ASTM D785 | 50-60 HD | ||
Heat shock(400℃/4hrs) | ASTM D 2671 | No drop/No flow | ||
Low temperature flexibility(-65℃/4hrs) | ASTM D 2671 | No cracking | ||
Electrical | Volume resistivity | ASTM D 2671 | ≥1018 Ω.cm | |
Dielectric strength | ASTM D2671 | ≥25 KV/mm | ||
Chemical | Flammability | ASTM D2671 | Not flammable | |
Organic dissolvent resistance | ASTM D543 | No change | ||
Effect by the sunshine | -- | No | ||
Typical application | ||||
Specially used in the surroundings of extreme electricity, chemistry and heat | ||||
Ordering | ||||
Standard color : Clear. | ||||
Standard packaging on spools and/or 1m/pc. | ||||
Please specify specification, color, quantity when ordering | ||||
Cross reference | ||||
Raychem/Tyco : RW-175/ TFE |